Thermoplastic composition made from a polyamide polymer obtained from a prepolymer and a chain extender and manufacturing method

ABSTRACT

A composition including at least one polyamide polymer obtained from at least one reactive polyamide prepolymer including at least one chain extender (PA1-All1-PA1), the polyamide polymer being prepared at a temperature T1 no lower than the temperature melting temperature or glass transition temperature of the polymer and having a mean molecular weight Mn1. The composition has a melt viscosity which can be modulated according to the temperature to which the composition is exposed, wherein the temperature is between T2 and T3, T2 and T3 being higher than T1, and the melt viscosity η2 or η′3 observed at the temperature T2 or T3, respectively, being lower than the melt viscosity η2 or η3 of the polyamide polymer, which does not include a chain extender and has the same mean molecular weight Mn1(PA1) observed at the same temperature T2 or T3. The composition includes one or more polyamides.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a divisional of U.S. application Ser. No. 15/304,589, filed on Oct. 17, 2016, which is a U.S. national stage of International Application No. PCT/FR2015/050999, filed on Apr. 14, 2015, which claims the benefit of French Application No. 1453359, filed on Apr. 15, 2014. The entire contents of each of U.S. application Ser. No. 15/304,589, International Application No. PCT/FR2015/050999, and French Application No. 1453359 are hereby incorporated herein by reference in their entirety.

TECHNICAL FIELD

The invention relates to a composition comprising at least one polyamide polymer derived from at least one reactive polyamide prepolymer comprising at least one chain extender, said composition having a melt viscosity which can be modulated according to the temperature to which said composition is subjected.

The invention also covers the polyamide polymer derived from said polyamide prepolymer with chain extender.

The invention also covers the use of a polyamide polymer derived from said prepolymer with said chain extender, for modulating the melt viscosity of a composition comprising said polyamide polymer and also the use of said composition for extrusion, injection-molding, or molding and in particular for easier impregnation of reinforcing fibers for the manufacture of composite.

The invention also covers a process for manufacturing said composition, a process for manufacturing a composite material, in particular mechanical parts or structural parts based on said material, by means of said composition, and the use of the composition of the invention for composite material parts and also the composite part which results therefrom and for applications in the motor vehicle, electrical and electronics, railway, marine, road transport, wind power, sport, aeronautical and aerospace, construction, panel and leisure fields.

BACKGROUND

EP 0 261 020 describes the use of reactive semicrystalline prepolymers based on PA 6, 11 and 12 for the manufacture of a thermoplastic composite by means of a pultrusion process. The prepolymers of aliphatic structure as described insufficient hot mechanical performance levels and are free of chain extender.

EP 1 988 113 describes a molding composition free of chain extender based on a 10T/6T copolyamide with:

-   -   40 to 95 mol % of 10T     -   5 to 40 mol % of 6T.

EP 0 581 642 describes polymers resulting from the addition of dicarboxy-terminated oligomers to bisoxazines or bisoxazolines, of which the viscosity of a given solution in meta-cresol at 30° C. at concentrations of 0.5 g/dl is less than 0.5 dl g⁻¹, but does not specify any melt viscosity.

US 2011306718 describes a process for the pultrusion of low-Tg reactive aliphatic polyamides combined with chain extenders having a polymeric structure bearing several (and indeed more than 2) anhydride or epoxyide functions. This document describes no non-polymeric extender. The chain extender is added during the impregnation of the fibers.

CN 102 234 373 describes a process for preparing biodegradable polyesteramides by chain extension.

KR 2008 0032357 describes a process for increasing the molecular weight of nylon using blocked diisocyanates as chain extender.

EP 2 586 585 describes thermoplastic composite materials having a Tg greater than or equal to 80° C., reinforced with synthetic fibers.

The use of compositions for obtaining good mechanical properties requires having available polymers, in particular polyamide, with high average molecular weights Mn. However, in the context of molding, the use of said polymers also requires an increased fluidity, i.e., a lower viscosity. It is thus necessary to increase the processing temperature in order to increase the fluidity, thereby causing degradation of said polymer.

SUMMARY

The drawbacks of the prior art, with the absence of a good compromise between mechanical performance levels and processing capacity (ease of transformation) at lower temperature with a shorter production cycle time are overcome by the solution of the present invention, which targets compositions, comprising at least one polyamide polymer derived from at least one reactive polyamide prepolymer comprising at least one chain extender (PA₁-All₁-PA₁), said polyamide polymer being prepared at a temperature T₁ greater than or equal to the temperature T_(m) or T_(g) of said polymer and having an average molecular weight Mn₁,

characterized in that said composition has a melt viscosity which can be modulated according to the temperature to which said composition is subjected,

said temperature being included from T₂ to T₃, T₂ and T₃ being greater than T₁,

and said melt viscosity η′₂ or η′₃ observed respectively at the temperature T₂ or T₃ being less than the melt viscosity η₂ or η₃ of said polyamide polymer, free of chain extender and having the same average molecular weight Mn₁(PA₁) observed at the same temperature T₂ or T₃,

allowing easier processing at lower temperatures for the same average molecular weight of polymer with savings regarding the overall energy balance of the processing process, a shorter production cycle time and an improved productivity, through an ability for rapid crystallization of said polyamide polymer and while maintaining the mechanical performance levels of said final materials at a high level, and modulation of the processing temperature for the same polyamide polymer derived from at least one reactive polyamide prepolymer comprising at least one chain extender according to the use and the applications desired for said polyamide polymer.

Consequently, the first subject of the invention relates to a composition, comprising at least one polyamide polymer derived from at least one reactive polyamide prepolymer comprising at least one chain extender (PA₁-All₁-PA₁), said polyamide polymer being prepared at a temperature T₁ greater than or equal to the temperature T_(m) or T_(g) of said polymer and having an average molecular weight Mn₁,

characterized in that said composition has a melt viscosity which can be modulated according to the temperature to which said composition is subjected,

said temperature being included from T₂ to T₃, T₂ and T₃ being greater than T₁,

and said melt viscosity η′₂ or η′₃ observed respectively at the temperature T₂ or T₃ being less than the melt viscosity η₂ or η₃ of said polyamide polymer, free of chain extender and having the same average molecular weight Mn₁(PA₁) observed at the same temperature T₂ or T₃.

Said composition is based on a polyamide polymer derived from at least one polyamide prepolymer comprising or consisting of at least one unit of amide A with the optional presence of at least one second unit of amide B different than A and optionally of at least one third (C) amide unit, these units being different than one another, and of at least one chain extender.

A second subject of the invention relates to a polyamide polymer derived from said polyamide prepolymer to which a chain extender has been added, i.e., resulting from the polymerization of said polyamide prepolymer to which said chain extender has been added.

A third subject relates to the use of a polyamide polymer with a chain extender, derived from said prepolymer with said chain extender, for modulating the melt viscosity of a composition comprising said polyamide polymer and also the use of said composition for extrusion, injection-molding, or molding and in particular for easier impregnation of reinforcing fibers for the manufacture of composite.

A fourth subject of the invention relates to a process for manufacturing said composition.

Another subject of the invention relates to a process for manufacturing a thermoplastic composite material and more particularly for manufacturing mechanical parts or structural parts based on said composite material.

Another subject of the invention relates to the use of the specific composition of PA of the invention for manufacturing a thermoplastic composite material of the same composition and more particularly mechanical or structural parts based on this material.

Another subject of the invention relates to the thermoplastic composite material which results from said composition for composite material.

Finally, the invention covers a mechanical part or structural part based on composite material obtained by means of the specific process of the invention or which results from the use of the specific composition of PA of the invention.

Consequently, the first subject relates to a composition, comprising at least one polyamide polymer derived from at least one reactive polyamide prepolymer comprising at least one chain extender (PA₁-All₁-PA₁), said polyamide polymer being prepared at a temperature T₁ greater than or equal to the temperature T_(m) or T_(g) of said polymer and having an average molecular weight Mn₁,

characterized in that said composition has a melt viscosity which can be modulated according to the temperature to which said composition is subjected,

said temperature being included from T₂ to T₃, T₂ and T₃ being greater than T₁,

and said melt viscosity η′₂ or η′₃ observed respectively at the temperature T₂ or T₃ being less than the melt viscosity η₂ or η₃ of said polyamide polymer, free of chain extender and having the same average molecular weight Mn₁(PA₁) observed at the same temperature T₂ or T₃,

and with:

said composition comprising or consisting of one or more polyamides, including random or block copolyamides which are polymers, and which comprise different amide units of formula A/(B)_(r)/(C)_(s), selected as follows:

-   -   A: is a repeating amide unit chosen from lactams or an amino         acid of C₆-C₁₄, an amide unit X.Y in which X represents at least         one diamine, said diamine being chosen from a linear or branched         aliphatic diamine, a cycloaliphatic diamine and an aromatic         diamine or a mixture thereof, and Y represents at least one         dicarboxylic acid, said diacid being chosen from:     -   an aliphatic diacid, a cycloaliphatic diacid and an aromatic         diacid,     -   said diamine and said diacid comprising from 4 to 36 carbon         atoms, advantageously from 6 to 18 carbon atoms;     -   B and C: are repeating amide units different than A, optionally         present depending on the value of r and s, r=0 or 1, s=0 or 1,         said amides units B and C being chosen from the same         constituents as for A, on the condition that when r and s=1,         then B and C are different,     -   the sum of the units A+B+C being equal to 100% by weight.

The sum of the molar contents in the absence of C amounts to A+B=100%, with A and B making it up to 100%.

In the absence of B and C, the molar content of A is 100%.

Said composition is free of reinforcing fibers and also of polymeric chain extender.

The temperature T_(m) denotes the melting temperature of a semicrystalline polyamide and T_(g) denotes the glass transition temperature of an amorphous polyamide.

The expression “average molecular weight Mn” is intended to mean the number-average molecular weight Mn, in particular determined by size exclusion chromatography.

(PA₁-All₁-PA₁) denotes the polyamide polymer comprising a reactive polyamide prepolymer comprising at least one chain extender. Said polyamide polymer may also be of formula (All₁-PA₁-All₁-PA₁-All₁) or (All₁-PA₁-All₁-PA₁), i.e., with at least one chain extender in the terminal position.

Advantageously, the melt viscosity ratio η′₃/η₃ observed at a temperature T₃ is less than the melt ratio η′₂/η₂ observed at a temperature T₂, T₃≥T₂+10° C.

Advantageously, the melt viscosity ratio η′₃/η₃ observed at a temperature T₃ is greater than the melt ratio η′₂/η₂ observed at a temperature T₂, T₃≤T₂−10° C.

Advantageously, the composition of the invention comprises or consists of at least one polyamide polymer derived from a polyamide prepolymer comprising at least one chain extender.

Advantageously, at least one prepolymer is present and a single chain extender is present.

Advantageously, a single prepolymer is present and at least one chain extender is present.

Advantageously, a single prepolymer is present and a single chain extender is present.

Advantageously, said polyamide polymer, when it is the only one present, comprises or consists of a single prepolymer and a single chain extender.

The term “which can be modulated” means that the melt viscosity of the composition is variable according to the temperature to which said composition is subjected.

The inventors have therefore found, unexpectedly, that a composition comprising or consisting of:

a polyamide polymer derived from at least one reactive polyamide prepolymer on which at least one chain extender is present (also called in the description: polyamide polymer with chain extender or polyamide polymer with extender), i.e., resulting from the polymerization of said at least one polyamide prepolymer on which at least one chain extender is present,

has not only a melt viscosity which can be modulated according to the temperature to which it is subjected, but also melt viscosities which are lower compared with the melt viscosity of the same polyamide polymer having the same molecular weight, but free of chain extender (also called in the description: polyamide polymer without chain extender or polyamide polymer without extender).

In other words:

-   -   either a polyamide polymer with a chain extender (PA₁-All₁-PA1)         having an average Mn equal to Mn₁,     -   or a polyamide polymer (PA₁) without chain extender having the         same Mn₁,         said PA₁-All₁-PA₁ and PA₁ being prepared at any temperature T         greater than or equal to T_(m) or T_(g),

if said PA₁-All₁-PA₁ and PA₁ are subjected to two different temperatures T₂ and T₃, and T₂ and T₃ being greater than T₁,

it is well known to those skilled in the art that the melt viscosities η₂ of PA₁ and η₃ of PA₁ obtained for respective temperatures T₂ and T₃ will be different, as will the melt viscosities η′₂ of PA₁-All₁-PA₁ and η′₃ of PA₁-All₁-PA₁ obtained for the respective temperatures T₂ and T₃.

However, entirely unexpectedly, the inventors have found that η′₂ is also less than η₂, just as η′₃ is less than η₃ although the average Mn₁ are identical.

In other words, the viscosity of PA₁-All₁-PA₁ is identical to that of PA₁ but at a lower temperature.

The expression “PA₁-All₁-PA₁” means that the chain extender is necessarily covalently integrated into the chain of the polyamide polymer and is not in the terminal position of the polyamide polymer.

Furthermore, the inventors have also found that the ratios of viscosities obtained between a composition comprising or consisting of a polyamide polymer free of chain extender and a composition comprising or consisting of a polyamide polymer with chain extender, at two different temperatures, are not constant.

In other words, η′₂/η₂≠η′₃/η₃ and depends on the temperature. Thus, η′₂/η₂>η′3/η₃ for T₃≥T₂+10° C. and η′₂/η₂<η′₃/η₃ for T₃≤T₂−10° C.

FIG. 1 summarizes these various properties.

Advantageously, when T₃≥T₂+10° C., then T₃ is at most 350° C., in particular at most 320° C., particularly at most 300° C.

When T₃≥T₂−10° C., then T₂ is at most 360° C., in particular at most 330° C., particularly at most 310° C.

This difference in viscosity obtained between said polyamide polymer with or without chain extender at the same temperature has the following advantages:

1) use of the composition comprising or consisting of a polyamide polymer with extender easier than use of that comprising or consisting of a polyamide polymer without extender and in particular at a lower temperature than the processing temperature of the polyamide without chain extender having the same average Mn;

2) possibility of obtaining compositions comprising or consisting of the same polyamide polymer with extender but having different melt viscosities and which can be used without distinction for extrusion, injection-molding, or molding, for varied applications, and allowing in particular easier impregnation of reinforcing fibers for the manufacture of composite materials, in particular mechanical or structural parts based on said material.

As Regards the Constituents (A), (B) and (C): Aliphatic Repeating Amide Unit:

In a first variant of the invention, the aliphatic amide unit A, B or C is obtained from an aminocarboxylic acid comprising from 6 to 14 carbon atoms. It can thus be chosen from 9-aminononanoic acid (denoted 9), 10-aminodecanoic acid (denoted 10), 11-aminoundecanoic acid (denoted 11) and 12-aminododecanoic acid (denoted 12); advantageously, the aminocarboxylic acid is 11-aminoundecanoic acid.

In a second variant of the invention, the aliphatic repeating unit A, B or C is obtained from a lactam comprising from 6 to 14 carbon atoms. It can thus be chosen from caprolactam (denoted 6), decanolactam (denoted 10), undecanolactam (denoted 11) and laurolactam or lauryllactam (denoted 12); advantageously, the lactam is undecanolactam.

More particularly preferably, the repeating unit A is obtained from a single aminocarboxylic acid or a single lactam.

Nonetheless, it is entirely possible to envision using, to obtain this same unit A, a mixture of two or more aminocarboxylic acids, a mixture of two or more lactams, but also a mixture of one, two or more aminocarboxylic acids with one, two or more lactams.

Repeating Unit A, B or C of X.Y Type

The repeating unit X.Y is a unit obtained from the polycondensation of at least one linear aliphatic diamine, or of at least one cycloaliphatic diamine or of at least one aromatic diamine or of a mixture of two or more thereof and of at least one aliphatic dicarboxylic acid or of at least one cycloaliphatic dicarboxylic acid or of at least one aromatic dicarboxylic acid.

The molar proportions of diamine and of dicarboxylic acid are preferentially stoichiometric.

The diamine and also the dicarboxylic acid each comprise from 4 to 36 carbon atoms and, advantageously, from 6 to 18 carbon atoms.

The aliphatic diamine used to obtain this repeating unit X. Y is an aliphatic diamine which has a linear main chain comprising at least 4 carbon atoms.

This linear main chain can, where appropriate, comprise one or more methyl and/or ethyl substituents; in said configuration, the term “branched aliphatic diamine” is used. In the case where the main chain comprises no substitute, the aliphatic diamine is termed “linear aliphatic diamine”.

Whether or not it comprises methyl and/or ethyl substituents on the main chain, the aliphatic diamine used to obtain this repeating unit X. Y comprises from 4 to 36 carbon atoms, advantageously from 4 to 18 carbon atoms, advantageously from 6 to 18 carbon atoms, advantageously from 6 to 14 carbon atoms.

When this diamine is a linear aliphatic diamine, it then corresponds to the formula H₂N—(CH₂)_(x)—NH₂ and can be chosen for example from butanediamine, pentanediamine, hexanediamine, heptanediamine, octanediamine, nonanediamine, decanediamine, undecanediamine, dodecanediamine, tridecanediamine, tetradecanediamine, hexadecanediamine, octadecanediamine and octadecenediamine. The linear aliphatic diamines that have just been mentioned may all be biobased within the meaning of standard ASTM D6866.

When this diamine is a branched aliphatic diamine, it can in particular be methyl-2 pentanediamine or 2-methyl-1,8-octanediamine.

The cycloaliphatic diamine can be chosen for example from bis(3,5-dialkyl-4-aminocyclohexyl)methane, bis(3,5-dialkyl-4-aminocyclohexyl)ethane, bis(3,5-dialkyl-4-aminocyclohexyl)propane, bis(3,5-dialkyl-4-aminocyclohexyl)butane, bis(3-methyl-4-aminocyclohexyl)methane or 3′-dimethyl-4,4′-diaminodicyclohexylmethane commonly called “BMACM” or “MACM” (and denoted B hereinafter) p-bis(aminocyclohexyl)methane commonly called “PACM” (and denoted P hereinafter), isopropylidenedi(cyclohexylamine) commonly called “PACP”, isophoronediamine (denoted IPD hereinafter) and 2,6-bis(aminomethyl)norbornane commonly called “BAMN”.

A non-exhaustive list of these cycloaliphatic diamines is given in the publication “Cycloaliphatic Amines” (Encyclopaedia of Chemical Technology, Kirk-Othmer, 4th Edition (1992), pp. 386-405).

The aromatic diamine can be chosen from 1,3-xylylenediamine and 1,4-xylylenediamine.

The dicarboxylic acid can be chosen from linear or branched aliphatic dicarboxylic acids, cycloaliphatic dicarboxylic acids, and aromatic dicarboxylic acids.

When the dicarboxylic acid is aliphatic and linear, it can be chosen from succinic acid (4), pentanedioic acid (5), adipic acid (6), heptanedioic acid (7), octanedioic acid (8), azelaic acid (9), sebacic acid (10), undecanedioic acid (11), dodecanedioic acid (12), brassylic acid (13), tetradecanedioic acid (14), hexadecanedioic acid (16), octadecanedioic acid (18), octadecenedioic acid (18), eicosanedioic acid (20), docosanedioic acid (22) and fatty acid dimers containing 36 carbons.

The fatty acid dimers mentioned above are dimerized fatty acids obtained by oligomerization or polymerization of unsaturated monobasic fatty acids bearing a long hydrocarbon-based chain (such as linoleic acid and oleic acid), as described in particular in document EP 0 471 566.

When the dicarboxylic acid is cycloaliphatic, it may comprise the following carbon backbones: norbornylmethane, cyclohexane, cyclohexylmethane, dicyclohexylmethane, dicyclohexylpropane, di(methylcyclohexyl) or di(methylcyclohexyl)propane.

When the dicarboxylic acid is aromatic, it can be chosen from terephthalic acid (denoted T), isophthalic acid (denoted I) and a naphthalenic acid.

According to one advantageous embodiment of the invention, A is an amide unit present in a molar content of 100%, and represents an aliphatic repeating unit obtained from a lactam or an amino acid, in particular chosen from PA6, PA11 and PA12.

According to one advantageous embodiment of the invention, A is an amide unit present in a molar content of 100%, and represents a repeating amide unit X.Y, in particular chosen from PA6.6, PA6.10, PA6.12, PA10.10 and 10.12.

According to one advantageous embodiment of the invention, A represents an amide unit present in a molar content ranging from 1% to 99%, B is an amide unit different than A, said unit B being present in a molar content ranging from 1% to 99%, and C is an optional amide unit different than A and than B and as defined above.

Advantageously:

-   -   A: is a major amide unit present in a molar content ranging from         55% to 95%, preferably from 55% to 85%, more preferentially from         55% to 80%, chosen from x.T units, where x is a linear aliphatic         C₄ to C₁₈ diamine, preferably chosen from C₆, C₉, C₁₀, C₁₁ and         C₁₂ and where T is terephthalic acid,     -   B: is an amide unit different than A, said unit B being present         in a molar content ranging from 5% to 45%, preferably from 15%         to 45%, more preferentially from 20% to 45%, depending on the Tm         of the polyamide based on unit A, and said amide unit B is         chosen from an aliphatic repeating unit obtained from a lactam         or an amino acid, in particular chosen from PA6, PA11 and PA 12         or a repeating amide unit X.Y, in particular chosen from PA6.6,         PA6.10, PA6.12, PA10.10 and 10.12.

More advantageously,

-   -   A: is a major amide unit present in a molar content ranging from         55% to 95%, preferably from 55% to 85%, more preferentially from         55% to 80%, even more preferentially from 55% to 75%, in         particular from 56% to 70%, chosen from x.T units, where x is a         linear aliphatic C₄ to C₁₈, preferably C₆, C₉, C₁₀, C₁₁ or C₁₂,         diamine and where T is terephthalic acid,     -   B: is an amide unit different than A, said unit B being present         in a molar content ranging from 5% to 45%, preferably from 15%         to 45%, more preferentially from 20% to 45%, even more         preferentially from 25% to 45%, in particular from 30% to 45%,         depending on the Tm of the polyamide based on unit A and with         said amide unit B being chosen from x′.T units where x′ is         chosen from:         -   B1) a branched aliphatic diamine bearing a single methyl or             ethyl, preferably methyl, branch (branching meaning the same             thing), in particular 2-methylpentamethylenediamine (MPMD)             or 2-methyloctamethylenediamine (MOMD), and having a main             chain length different by at least two carbon atoms compared             with the main chain length of the diamine x of said             associated unit A, preferably x′ (according to B1)) being             MPMD or         -   B2) m-xylylenediamine (MXD) or         -   B3) a linear aliphatic C₄ to C₁₈ diamine, preferably with a             difference of at least two carbon atoms between the chain of             diamine x of said unit A and the chain of diamine x′ of said             unit B,     -   and preferably, said unit B is chosen from x′.T units, where x′         is MPMD according to option B1) or MXD according to option B2)         or a linear aliphatic diamine as defined above according to         option B3) or more preferentially x′ is MPMD according to B1) or         MXD according to B2) and even more preferentially x′ is MXD         according to B2),     -   C: optional amide unit different than A and than B as defined         above,         and under the condition that the sum of the molar contents A+B+C         is equal to 100%.

According to a first possibility, in said composition of the invention, said polyamide polymer comprises said amide unit according to C, different than A and than B, where the unit C as defined above is present. C can be present in a molar content ranging up to 30%, preferably up to 25%, preferably up to 20%, more preferentially up to 15%, relative to the total molar content of the polyamide.

When the unit C is present and corresponds to x′T with x′ as defined above for the unit B, in this case C being different than B by definition, said unit C can be based on x′ which is defined according to B1 and in this case, said unit B may have x′ defined according to either B2 or B3. If C is based on x′ according to B2, in this case the unit B may be based on x′ which is according to B1 or B3. If C is based on x′ according to B3, in this case the unit B may be based on x′ which is defined according to B1 or B2.

More particularly, in this unit C of said composition, said aromatic structure may be chosen for example from the isophthalic and/or naphthalenic structure. A terephthalic structure is possible in particular for the diacid component when the diamine is cycloaliphatic. Said cycloaliphatic structure may be chosen from a structure based on a cyclohexane ring or a structure based on a decahydronaphthalenic ring (hydrogenated naphthalenic structure).

Preferably, the structure of C is derived from an aliphatic diamine and from a cycloaliphatic and/or aromatic diacid, for example as defined above, or from a diacid and from a cycloaliphatic diamine, for example as defined above. More particularly, said unit C is chosen from the units derived:

-   -   from a cycloaliphatic diamine and from terephthalic acid or     -   from a diacid chosen from isophthalic acid and naphthenic acid         or based on cyclohexane and on a diamine x or x′ as defined         above for the units A and B respectively.

According to another variant of the composition of the invention, said unit C is present in a molar content that can range up to 70%, in particular up to 40%, in particular up to 30%, preferably up to 20%, relative to the total molar content of the polyamide. Thus, according to this variant, said composition comprises said unit C as defined above, in particular chosen from: C₆ to C₁₂, preferably C₆, C₁₁ and C₁₂, amino acids or lactams, or mixtures thereof, or units derived from the reaction of a C₆ to C₁₈, preferably C₆ to C₁₂, linear aliphatic diacid and of a C₆ to C₁₈, preferably C₆ to C₁₂, linear aliphatic diamine, and preferably with the units A and B being respectively based on the diamines x and x′ as defined above.

Preferably, the unit C, when it is present, is in a molar content of less than 40% relative to the total molar content of the polyamide as defined according to the invention.

Preferably, said amide unit A, as defined according to the invention above and below, is present in a molar content ranging from 55% to 80%, more preferentially from 55% to 75%, even more preferentially from 55% to 70%, relative to all of the units of said polyamide polymer as defined above according to the invention.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 95% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 85% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 80% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 75% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 5% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 15% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 20% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 25% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the composition comprises or consists of the units A in a proportion of from 55% to 70% and B in a proportion of from 30% to 45%, the sum of the molar contents of A+B being equal to 100%.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C in a molar content ranging up to 30%, relative to all of the units of said polymer.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C in a molar content ranging up to 25%, relative to all of the units of said polymer.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C in a molar content ranging up to 20%, relative to all of the units of said polymer.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C in a molar content ranging up to 15%, relative to all of the units of said polymer.

According to a first preferred option of the composition according to the invention described above, said composition has a unit B with x′ defined according to option B1 described above, in particular with MPMD being a more preferred diamine for said unit B. The unit A remains as defined above, i.e., x.T, with x a C₄ to C₁₈, preferably C₉, C₁₀, C₁₁ or C₁₂, linear aliphatic diamine.

According to a second preferred option of said composition, it has a unit B where x′ is MXD according to option B2 defined above. The unit A remains as defined for the first option mentioned. This second option constitutes, together with the first mentioned above, the options that are the most preferred of the invention and in particular this second option is the most preferred of the invention.

A third preferred option is that where B is defined according to option B1 or B2 or B3 as defined above and with the presence of a unit C as defined above as a replacement for B and up to 25 mol %, preferably up to 20 mol %, more preferentially up to 15 mol %, and in particular with B being defined according to the first or second option as defined above.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C as partial replacement for B and in a molar content ranging up to 25%, relative to said unit B.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C as partial replacement for B and in a molar content ranging up to 20%, relative to said unit B.

Advantageously, the compositions comprising or consisting of the units A and B, the sum of the molar contents of A+B being equal to 100%, defined above, also comprise a unit C as partial replacement for B and in a molar content ranging up to 15%, relative to said unit B.

Even more preferentially, said polyamide composition is based on the units A and B selected as follows:

-   -   for the unit A, which is 6T, said unit B is selected from: 9T,         10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, preferably 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T,         MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a         molar content of B ranging from 20% to 45%,     -   for the unit A, which is 9T, said unit B is selected from: 6T,         10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, preferably 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T,         MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a         molar content of B ranging from 30% to 45%,     -   for the unit A, which is 10T, said unit B is selected from: 6T,         9T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         preferably 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, more preferentially MPMD.T or MXD.T, with a molar content         of B ranging from 25% to 45%,     -   for the unit A, which is 11T, said unit B is selected from: 6T,         9T, 10T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         preferably 9T, 13T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         more preferentially MPMD.T or MXD.T, with a molar content of B         ranging from 20% to 45%,     -   for the unit A, which is 12T, said unit B is selected from: 6T,         9T, 10T, 11T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         preferably 9T, 10T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, more preferentially MPMD.T or MXD.T, with a molar content         of B ranging from 20% to 45%.

According to this selection, a first more particular composition of the invention can be defined with the unit A being a unit 6T and the unit B being selected from: 9T, 10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a molar content of B ranging from 20% to 45%.

A second particular composition corresponds to a unit A which is a unit 9T, the unit B being selected from: 10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a molar content of B ranging from 30% to 45%. A third particular composition corresponds to a unit A which is a unit 10T, the unit B being selected from: 9T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a molar content of B ranging from 25% to 45%. A fourth particular composition corresponds to a unit A which is a unit 11T, the unit B being selected from: 9T, 10T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 9T, 13T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a molar content of B ranging from 20% to 45%. Finally, another particular composition corresponds to a unit A which is a unit 12T, the unit B being selected from: 9T, 10T, 11T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 9T, 10T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a molar content of B ranging from 20% to 45%.

According to a preferred fifth option, the unit A remains as defined above, i.e. x.T, with x a linear aliphatic C₄ to C₁₈, preferably C₆, C₉, C₁₀, C₁₁ or C₁₂, amine, the unit B corresponds to x′.T with x′ being B3) a linear aliphatic C₄ to C₁₈ diamine and the unit C is present and in particular chosen from C₆ to C₁₂, preferably C₆, C₁₁ and C₁₂, lactams or amino acids, or mixtures thereof, or the units resulting from the reaction of a linear aliphatic C₆ to C₁₈, preferably C₆ to C₁₂ diacid and of a linear aliphatic C₆ to C₁₈, preferably C₆ to C₁₂, diamine and preferably with the units A and B being respectively based on the diamines x and x′ as defined above.

Preferably, the unit C, in this fifth option, is in a molar content of less than 40%, in particular less than 30%, in particular less than 20%, relative to the total molar content of the polyamide as defined according to the invention.

Advantageously, one of the preferred compounds of this fourth option is 10.T/6.T/11.

Said composition comprises or consists of a polyamide polymer resulting from the polymerization of the reaction product of:

-   a1) at least one prepolymer of said polyamide polymer as already     defined above with this prepolymer bearing n identical end reactive     functions X1, chosen from: —NH₂ (amine), —CO₂H (carboxy) and —OH     (hydroxyl), preferably —NH₂ (amine) and —CO₂H (carboxy), with n     being 1 to 3, preferably from 1 to 2, more preferentially 1 or 2,     more particularly 2, with -   a2) at least one chain extender Y₁-A′-Y₁, with A′ being a     hydrocarbon-based biradical of non-polymeric structure (neither     polymer nor oligomer nor prepolymer), bearing 2 identical end     reactive functions Y₁, reactive by polyaddition (without elimination     of reaction by-product) with at least one function X₁ of said     prepolymer a1), preferably having a molecular weight of less than     500 and more preferentially less than 400,     in particular, Y₁ is chosen from: oxazine, oxazoline, oxazolinone,     oxazinone, imidazoline, epoxy, isocyanate, maleimide, cyclic     anhydride, in particular oxazine, oxazoline, oxazolinone, oxazinone,     imidazoline, epoxy, maleimide, cyclic anhydride, and preferentially     X₁ is CO₂H and Y₁ is chosen from an epoxy and an oxazoline.

NH₂ (amine) signifies a primary and secondary amine.

As suitable examples of extenders a2) as a function of the functions X₁ borne by said semicrystalline polyamide prepolymer a1), mention may be made of the following:

-   -   when X₁ is NH₂ or OH, preferably NH₂:         -   either the chain extender Y₁-A′-Y₁ corresponds to             -   Y₁ chosen from the groups: maleimide, isocyanate which                 is optionally blocked, oxazinone and oxazolinone, and                 cyclic anhydride, preferably oxazinone and oxazolinone,                 in particular maleimide, oxazinone and oxazolinone, and                 cyclic anhydride, preferably oxazinone and oxazolinone         -   and             -   A′ is a carbon-based spacer or a carbon-based radical                 bearing the reactive functions or groups Y₁, chosen                 from:                 -   a covalent bond between two functions (groups) Y in                     the case where Y₁=oxazinone and oxazolinone or                 -   an aliphatic hydrocarbon-based chain or an aromatic                     and/or cycloaliphatic hydrocarbon-based chain, the                     latter two comprising at least one optionally                     substituted ring of 5 or 6 carbon atoms, with                     optionally said aliphatic hydrocarbon-based chain                     optionally having a molecular weight of 14 to 200                     g·mol⁻¹         -   or the chain extender Y₁-A′-Y₁ corresponds to Y which is a             caprolactam group and to A′ which can be a carbonyl radical             such as carbonyl biscaprolactam or to A′ which can be a             terephthaloyl or an isophthaloyl,         -   or said chain extender Y₁-A′-Y₁ bears a cyclic anhydride             group Y, and preferably this extender is chosen from a             cycloaliphatic and/or aromatic carboxylic dianhydride and             more preferentially it is chosen from:             ethylenetetracarboxylic dianhydride, pyromellitic             dianhydride, 3,3′,4,4′-biphenyltetracarboxylic dianhydride,             1,4,5,8-naphtalenetetracarboxylic dianhydride,             perylenetetracarboxylic dianhydride, 3,3′,4,4′-benzophenone             tetracarboxylic dianhydride,             1,2,3,4-cyclobutanetetracarboxylic dianhydride,             hexafluoroisopropylidene bisphthalic dianhydride,             9,9-bis(trifluoromethyl)xanthenetetracarboxylic dianhydride,             3,3′,4,4′-diphenylsulfonetetracarboxylic dianhydride,             bicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic dianhydride,             1,2,3,4-cyclopentanetetracarboxylic dianhydride,             3,3′,4,4′-diphenyl ether tetracarboxylic dianhydride, or             mixtures thereof and     -   when X₁ is COOH:         -   said chain extender Y₁-A′-Y₁ corresponds to:             -   Y₁ chosen from the groups: oxazoline, oxazine,                 imidazoline, aziridine, such as 1,1′-iso- or                 terephthaloyl-bis(2-methylaziridine) or epoxy,             -   A′ being a carbon-based spacer (radical) as defined                 above.

More particularly, when, in said extender Y₁-A′-Y₁, said function Y₁ is chosen from oxazinone, oxazolinone, oxazine, oxazoline or imidazoline, in particular oxazoline, in this case, in the chain extender represented by Y₁-A′-Y₁, A′ can represent an alkylene such as —(CH₂)_(m)— with m ranging from 1 to 14 and preferably from 2 to 10 or A′ can represent a cycloalkylene and/or an arylene which is substituted (alkyl) or unsubstituted, for instance benzenic arylenes, such as o-, m- or p-phenylenes, or naphthalenic arylenes, and preferably A′ is an arylene and/or a cycloalkylene.

In the case where Y₁ is an epoxy, the chain extender can be chosen from bisphenol A diglycidyl ether (DGEBA), and its (cycloaliphatic) hydrogenated derivative bisphenol F diglycidyl ether, tetrabromo bisphenol A diglycidyl ether, or hydroquinone diglycidyl ether, ethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, butylene glycol diglycidyl ether, neopentyl glycol diglycidyl ether, 1,4-butanediol diglycidyl ether, 1,6-hexanediol diglycidyl ether, cyclohexanedimethanol diglycidyl ether, polyethylene glycol diglycidyl ether of Mn<500, polypropylene glycol diglycidyl ether of Mn<500, polytetramethylene glycol diglycidyl ether of Mn<500, resorcinol diglycidyl ether, neopentylglycol diglycidyl ether, bisphenol A polyethylene glycol diglycidyl ether of Mn<500, bisphenol A polypropylene glycol diglycidyl ether of Mn<500, diglycidyl esters of a dicarboxylic acid, such as terephthalic acid glycidyl ester, or epoxidized diolefins (dienes) or fatty acids with a double epoxidized ethylenic unsaturation, diglycidyl 1,2-cyclohexanedicarboxylate, and mixtures thereof.

In the case of carbonyl- or terephthaloyl- or isophthaloyl-biscaprolactam as chain extender Y₁-A′-Y₁, the preferred conditions avoid the elimination of by-product, such as caprolactam during said polymerization and processing in the molten state.

In the optional case mentioned above where Y₁ represents a blocked isocyanate function, this blocking can be obtained using agents for blocking the isocyanate function, for instance epsilon-caprolactam, methyl ethyl ketoxime, dimethylpyrazole, or diethyl malonate.

Likewise, in the case where the extender is a dianhydride which reacts with a prepolymer P(X₁)n where X₁═NH₂, the preferred conditions avoid any formation of an imide ring during the polymerization and during the processing in the molten state.

For X₁═OH or NH₂, the group Y₁ is preferably chosen from: isocyanate (nonblocked), oxazinone and oxazolinone, more preferentially oxazinone and oxazolinone, with, as spacer (radical), A′ which is as defined above.

As examples of chain extenders bearing oxazoline or oxazine reactive functions Y that are suitable for the implementation of the invention, reference may be made to those described under references “A”, “B”, “C” and “D” on page 7 of application EP 0 581 642, and also to the processes for preparing same and the modes of reaction thereof which are disclosed therein. “A” in this document is bisoxazoline, “B” bisoxazine, “C” 1,3 phenylene bisoxazoline and “D” 1,4-phenylene bisoxazoline.

By way of example, in the case where X₁═CO₂H and the chain extender Y₁-A′-Y₁ is 1,4-phenylene bisoxazoline, the reaction product obtained has at least one recurring unit having the following structure:

—O—C(O)—P—C(O)—O—R₁—NH—C(O)-A′-C(O)—NH—R₁—

in which: P is an acid-terminated polyamide HO—C(O)—P—C(O)—OH obtained from the amide units (A), (B) or (C), R₁ is (CH₂)₂, and A′ is a phenyl.

As examples of chain extenders bearing imidazoline reactive functions Y that are suitable for the implementation of the invention, reference may be made to those described (“A” to “F”) on pages 7 to 8 and table 1 on page 10 of application EP 0 739 924, and also to the processes for preparing same and the modes of reaction thereof which are disclosed therein.

As examples of chain extenders with a reactive function Y₁=oxazinone or oxazolinone which are suitable for the implementation of the invention, reference may be made to those described under references “A” to “D” on pages 7 to 8 of application EP 0 581 641, and also to the processes for preparing same and the modes of reaction thereof which are disclosed therein.

As examples of oxazinone (6-atom ring) and oxazolinone (5-atom ring) groups Y₁ which are suitable, mention may be made of the groups Y₁ derived from: benzoxazinone, from oxazinone or from oxazolinone, with, as spacer, A′ which can be a single covalent bond with respective corresponding extenders being: bis(benzoxazinone), bisoxazinone and bisoxazolinone.

A′ may also be a C₁ to C₁₄, preferably C₂ to C₁₀, alkylene, but preferably A′ is an arylene and more particularly it may be a phenylene (substituted with Y₁ in positions 1,2 or 1,3 or 1,4) or a naphthalene radical (disubstituted with Y₁) or a phthaloyl (iso- or terephthaloyl) or A′ may be a cycloalkylene.

For the functions Y₁ such as oxazine (6-membered ring), oxazoline (5-membered ring) and imidazoline (5-membered ring), the radical A′ may be as described above with A′ possibly being a single covalent bond and with the respective corresponding extenders being: bisoxazine, bisoxazoline and bisimidazoline. A′ may also be a C₁ to C₁₄, preferably C₂ to C₁₀, alkylene. The radical A′ is preferably an arylene and more particularly it may be a phenylene (substituted with Y₁ in positions 1,2 or 1,3 or 1,4) or a naphthalene radical (disubstituted with Y₁) or a phthaloyl (iso- or terephthaloyl) or A′ may be a cycloalkylene.

In the case where Y₁=aziridine (3-atom nitrogenous heterocycle equivalent to ethylene oxide with replacement of the ether —O— with —NH—), the radical A′ may be phthaloyl (1,1-iso- or tere-phthaloyl) with, as an example of an extender of this type, 1,1′ isophtaloylbis(2-methylaziridine).

The presence of a catalyst of the reaction between said prepolymer P(X)n and said extender Y₁-A′-Y₁ in a content ranging from 0.001% to 2%, preferably from 0.01% to 0.5%, relative to the total weight of the two co-reactants mentioned, can accelerate the (poly)addition reaction and thus shorten the production cycle. Such a catalyst can be chosen from: 4,4′-dimethylaminopyridine, p-toluenesulfonic acid, phosphoric acid, NaOH and optionally those described for a polycondensation or transesterification as described in EP 0 425 341, page 9, lines 1 to 7.

According to a more particular case of the choice of said extender, A′ can represent an alkylene, such as —(CH₂)_(m)— with m ranging from 1 to 14 and preferably from 2 to 10, or represents an alkyl-substituted or unsubstituted arylene, such as benzenic arylenes (such as o-, m- or p-phenylenes) or naphthalenic arylenes (with arylenes: naphthalenylenes). Preferably, A′ represents an arylene which may be substituted or un-substituted benzenic or naphthalenic.

As already specified, said chain extender (a2) has a non-polymeric structure and preferably a molecular weight of less than 500, more preferentially less than 400.

Said reactive prepolymers of said composition, mentioned above, have a number-average molecular weight Mn ranging from 500 to 10 000, preferably from 1000 to 6000, determined in particular by calculation on the basis of the content of end functions, determined by potentiometric titration in solution, and the functionality of said prepolymers. The weights Mn can also be determined by size exclusion chromatography or by NMR.

The content of said extender in said polyamide polymer ranges from 1% to 20%, in particular from 5% to 20%, particularly from 10% to 20%.

In the case of the reactive compositions of the invention according to definition a), said reactive prepolymers are prepared by conventional polycondensation reaction between the diamine and corresponding diacid components and optionally amino acids or lactams, while respecting the nature and proportions of the units A and B and optionally C according to the invention. The prepolymers bearing amine and carboxy functions X₁′ and Y₁′ on the same chain can be obtained, for example, by adding a combination of monomers (amino acid, diamine, diacid) having in total an equal amount of amine and carboxy units. Another route for obtaining these prepolymers bearing a function X₁′ and a Y₁′ is, for example, by combining a prepolymer bearing 2 identical functions X₁′=amine, with a diacid prepolymer bearing Y₁′: carboxy, with an overall molar content of acid functions equal to that of the starting amine functions X₁′.

To obtain prepolymers functionalized with identical (amine or carboxy) functions on the same chain, it is sufficient to have an excess of diamine (or of overall amine functions) to have amine end functions or an excess of diacid (or of overall carboxy functions) to have carboxy end functions.

In the case of a prepolymer P(X₁)n with n identical functions X₁, the functionality 1 can be obtained in the presence of a blocking mono functional component (monoacid or monoamine depending on the nature of X₁=amine or carboxy).

A functionality n=2 can be obtained from bifunctional components: diamines and diacids with excess of one to fix X₁ depending on this excess.

For n=3 for example, for a prepolymer P(X₁)n, the presence of a trifunctional component is necessary, for example the presence of a triamine (one mol per prepolymer chain) with a diamine in the reaction with a diacid. The preferred functionality for P(X₁)n is n=2.

Said polyamide polymer is derived from a reactive polyamide prepolymer comprising a chain extender by polymerization of the reactive precursor composition, this reactive prepolymer having an Mn at least two times lower than that of said polyamide polymer. The number-average molecular weight Mn of said polyamide polymer of said composition is preferably in a range of from 10 000 to 40 000, preferably from 12 000 to 30 000, determined in particular by calculation on the basis of the content of end functions, determined by potentiometric titration in solution, and the functionality of said prepolymers.

According to one advantageous embodiment, said composition also has an average molecular weight which can be modulated according to the temperature to which it is subjected.

According to one advantageous embodiment, the composition of the invention defined above comprises or consists of a polyamide polymer derived from a prepolymer to which has been added a chain extender Y₁-A′-Y₁ which is chosen from phenylene-bisoxazolines, preferably 1,3-phenylene-bis(2-oxazoline) or 1,4-phenylene-bis(2-oxazoline) (PBO).

The term “which can be modulated” signifies in this case that the average molecular weight of the polyamide polymer of the composition is variable as a function of the temperature to which said composition is subjected.

In other words, a polyamide polymer with a chain extender of PBO type (PA-PBO-PA) having an average molecular weight Mn₁, when it is prepared at a temperature T₁ greater than or equal to T_(m) or T_(g), has an average molecular weight Mn₂, with Mn₂≤Mn₁, if this same PA-PBO-PA is this time subjected to a temperature T₂, T₂ being greater than or equal to T_(m), and T₂≥T₁ and conversely, Mn₂≥Mn1, if T₂≤T₁.

Consequently, the inventors have found that not only can the melt viscosity of the composition be modulated, but also the average molecular weight of said polyamide polymer thus provides the advantage of being able to obtain compositions with a viscosity and/or an average molecular weight of the polyamide polymer of said composition which can be modulated, thus allowing varied uses for extrusion, injection-molding or molding and varied applications of said composition.

The composition according to the invention may comprise fillers other than reinforcing fibers and additives.

Among the suitable fillers, mention may for example be made of: inorganic or organic fillers: carbon black, carbon nanotubes (CNTs), carbon nanofibrils, glass beads, ground recycled polymers in powder form.

Among the suitable additives, mention may be made of: additives which absorb in the UV or IR range so as to allow welding of the composite obtained, by a laser technology (UV or IR), and heat stabilizers chosen from antioxidants of sterically hindered phenol or sterically hindered amine (HALS) type. The function of these stabilizers is to prevent thermal oxidation and considerable photooxidation and degradation of the polyamide.

The second subject of the invention relates to the reactive polyamide polymer derived from a prepolymer to which a chain extender has been added as defined according to the composition above. This polyamide polymer is by definition one of the essential components of the composition of the thermoplastic composite material of the present invention and is therefore part of the invention as a product linked to the present invention with the same common inventive concept in the face of the same technical problem to be solved.

The polyamide polymer may be in the form of granules or powder.

The third subject of the invention relates to the use of at least one polyamide polymer as defined according to the composition above, for modulating the melt viscosity of a composition comprising said polyamide polymer.

The use of said prepolymer at variable temperatures makes it possible to obtain compositions which have different viscosities.

Advantageously, the use of said polyamide prepolymer makes it possible to modulate the melt viscosity of a composition comprising said polyamide polymer and the average molecular weight of said polyamide polymer.

Advantageously, said polyamide prepolymer comprises a chain extender Y₁-A′-Y₁ which is 1,3-phenylene-bis(2-oxazoline) or 1,4-phenylene-bis(2-oxazoline). The third subject also relates to the use of a composition as defined above, for extrusion, injection-molding, or molding for the manufacture of mechanical or structural parts based on said composite material, and in particular for easier impregnation of reinforcing fibers for the manufacture of composite. Advantageously, said mechanical or structural parts of said composite material concern applications in the motor vehicle, electrical or electronics, railway, marine (maritime) and wind power fields, the photovoltaic field, the solar energy field, including solar panels and components of solar power stations, the sport field, the aeronautical and aerospace field, and the road transport (regarding trucks), construction, civil engineering, panel, and leisure fields.

Advantageously, said parts for applications in the motor vehicle industry are parts under an engine hood for transporting fluid, in particular in air intake devices, cooling devices (cooling for example by air, cooling liquid, etc.), and devices for transporting or transferring fuels or fluids (such as oil, water, etc.).

Advantageously, said mechanical or structural parts for applications in the electrical or electronics industry are electrical and electronic goods, such as encapsulated solenoids, pumps, telephones, computers, printers, fax machines, modems, monitors, remote controls, cameras, circuit breakers, electrical cable jackets, optical fibers, switches, or multimedia systems. These elements of electrical and electronic goods cover not only the structural parts of such goods (casings, housings, etc.), but also their optional associated accessories (earphones, connecting elements, cables, etc.).

More particularly, three more preferred applications can be distinguished according to the temperature at which said parts made of composite material according to the invention are used:

-   -   in the wind power industry, with a Tg of said thermoplastic         matrix polyamide of at least 90° C.     -   in the motor vehicle industry, with a Tg of said polyamide of at         least 100° C.     -   in the aeronautical industry, with a Tg of said polyamide of at         least 120° C.

This means that, for a Tg of at least 100° C., it can have two possible applications: motor vehicle industry and wind power industry, and if the Tg is at least 120° C., it can have an application in the wind power and motor vehicle industries, in addition to the aeronautical industry.

The use of the composition of the invention therefore makes it possible to prepare various objects such as a tube, pipe, profiled part, textile fiber, plate, sheet, or film, by extrusion, or objects for the applications defined above, by injection-molding or molding.

The fourth subject of the invention relates to a process for manufacturing a thermoplastic composite material, in particular a mechanical part or a structural part based on said material, having a composition as defined according to the invention as set out above, which process comprises at least one step of molding or of processing at least one composition as defined above according to the invention, at a temperature T which makes it possible to obtain a desired viscosity q.

More particularly, said process can comprise the following steps:

-   -   i) melt impregnation of a fibrous reinforcement with a         composition as defined above according to the invention but not         comprising said fibrous reinforcement in an open or closed mold         or outside the mold, in order to obtain a composition as defined         according to the invention comprising, in addition, an         impregnated fibrous reinforcement,     -   ii) processing or molding of said composition of step i), so as         to form the final composite part in a mold or with another         processing system.

Advantageously, the polyamide polymer of the composition of the invention has a glass transition temperature Tg of less than or equal to 75° C. and a melting temperature from 150° C. to less than 250° C. or a Tg of greater than 75° C., in particular of at least 80° C. and preferably of from 100 to 200° C., more preferentially from 110 to 200° C., in particular from 110° C. to less than 180° C., said process comprising:

i) a step of bulk melt impregnation with at least one composition as defined above, in particular having a viscosity at the bulk melt impregnation temperature not exceeding 200 Pa·s, preferably not exceeding 150 Pa·s,

ii) a step of cooling and obtaining a fibrous pre-impregnate,

iii) a step of processing and final forming of said composite material.

In said process according to the invention, said processing can preferably be carried out according to an RTM, S-RIM, injection-compression molding or pultrusion process or by infusion molding, in particular in the case of a composition.

Advantageously, said processing step is carried out by thermocompression of pre-impregnates under reduced pressure.

The reinforcing fibers or fibrous reinforcement may be an assembly of fibers, preferably of long fibers, i.e., fibers having an aspect ratio defined by the ratio of length to diameter of the fiber, which means that these fibers have a circular cross-section, greater than 1000, preferably greater than 2000. In this assembly, the fibers may be continuous, or in unidirectional (UD) or multidirectional (2D, 3D) reinforcement form. In particular, they may be in the form of fabrics, sheets, strips, or braids and may also be cut, for example in the form of nonwovens (mats) or in the form of felts.

These reinforcing fibers may be chosen from:

-   -   mineral fibers, said fibers having high melting temperatures Tm′         above the melting temperature Tm of said semicrystalline         polyamide of the invention and above the polymerization and/or         processing temperature;     -   polymeric fibers or polymer fibers having a melting temperature         Tm′, or if not Tm′, a glass transition temperature Tg′, above         the polymerization temperature or above the melting temperature         Tm of said semicrystalline polyamide constituting said matrix of         the composite and above the processing temperature;     -   or mixtures of the abovementioned fibers.

As mineral fibers suitable for the invention, mention may be made of carbon fibers, which includes fibers of nanotubes or carbon nanotubes (CNTs), carbon nanofibers or graphenes; silica fibers such as glass fibers, in particular of E, R or S2 type; boron fibers; ceramic fibers, in particular silicon carbide fibers, boron carbide fibers, boron carbonitride fibers, silicon nitride fibers, boron nitride fibers, basalt fibers; fibers or filaments based on metals and/or alloys thereof; fibers of metal oxides, in particular of alumina (Al₂O₃); metallized fibers such as metallized glass fibers and metallized carbon fibers, or mixtures of the abovementioned fibers.

More particularly, these fibers may be chosen as follows:

-   -   the mineral fibers may be chosen from: carbon fibers, carbon         nanotube fibers, glass fibers, in particular of E, R or S2 type;         boron fibers, ceramic fibers, in particular silicon carbide         fibers, boron carbide fibers, boron carbonitride fibers, silicon         nitride fibers, boron nitride fibers, basalt fibers, fibers or         filaments based on metals and/or alloys thereof, fibers based on         metal oxides such as Al₂O₃, metallized fibers such as metallized         glass fibers and metallized carbon fibers, or mixtures of the         abovementioned fibers, and     -   the polymer fibers or polymeric fibers, under the abovementioned         condition, are chosen from:         -   thermosetting polymer fibers and more particularly those             chosen from: unsaturated polyesters, epoxy resins, vinyl             esters, phenolic resins, polyurethanes, cyanoacrylates, and             polyimides, such as bismaleimide resins, or aminoplasts             resulting from the reaction of an amine such as melamine             with an aldehyde such as glyoxal or formaldehyde,         -   thermoplastic polymer fibers, more particularly chosen from:             polyethylene terephthalate (PET), polybutylene terephthalate             (PBT), high-density polyolefins such as polyethylene (PET),             polypropylene (PP) and PET/PP, PVOH (polyvinyl alcohol)             copolymers,         -   fibers of polyamides corresponding to one of the formulae:             6, 11, 12, 6.10, 6.12, 6.6 and 4.6,         -   fibers of aramids (such as Kevlar®) and aromatic polyamides             such as those corresponding to one of the formulae: PPD.T,             MPD.I, PAA and PPA, with PPD and MPD being respectively p-             et m-phenylenediamine, PAA being polyarylamides and PPA             being polyphthalamides,         -   fibers of polyamide block copolymers such as             polyamide/polyether, fibers of polyaryl ethers ketones             (PAEKs) such as polyether ether ketone (PEEK), polyether             ketone ketone (PEKK) or polyether ketone ether ketone ketone             (PEKEKK).

The preferred reinforcing fibers are long fibers (with a circular cross-section) chosen from: carbon fibers, including those which are metallized, glass fibers, including those which are metallized, of E, R, S2 type, fibers of aramids (such as Kevlar®) or aromatic polyamides, polyaryl ether ketone (PAEK) fibers, such as polyether ether ketone (PEEK) fibers, polyether ketone ketone (PEKK) fibers, polyether ketone ether ketone ketone (PEKEKK) fibers, or mixtures thereof.

The fibers that are more particularly preferred are chosen from: glass fibers, carbon fibers, ceramic fibers, and aramid fibers (such as Kevlar®), or mixtures thereof. These fibers have a circular cross-section.

Said fibers can represent contents of from 40% to 70% by volume and preferably from 50% to 65% by volume of said composite material.

The fiber assembly may be random (mat), unidirectional (UD) or multidirectional (2D, 3D, or the like). The grammage thereof, i.e., the weight thereof per square meter, can range from 100 to 1000 g/m², preferably from 200 to 700 g/m². The fibers may be in woven or nonwoven form, in particular in the form of reinforcing cloths and fabrics. They can in particular be assembled and linked in the form of a preform already having the shape of the final part. As suitable linking agent, use may be made of a composition according to a) or b) and, failing this, a linking agent compatible with said composition (composition a) or b)).

The present invention also covers a thermoplastic composite material resulting from the use of at least one composition for thermoplastic composite material as defined above according to the present invention.

Lastly, the invention relates to a mechanical part or a structural part made of thermoplastic composite material, which results from the use of at least one composition of the invention as defined above or from the use of a semicrystalline polyamide polymer as defined according to the invention or of a thermoplastic composite material as defined above, or which part is obtained by means of a process as defined above according to the invention.

More particularly, said structural part is a motor vehicle part post-treated by cataphoresis, in particular with a Tg of at least 90° C.

According to another option, it is a part for wind power, in particular with a Tg of at least 100° C.

According to a third particular option, it is a part for the aeronautical industry, in particular with a Tg of at least 120° C.

Methods for Determining the Characteristics Mentioned

-   -   The melt viscosity of the prepolymer or of the precursor         composition is measured according to the reference manual of the         constructor of the measuring instrument used, which is a Physica         MCR301 Rheometer, under nitrogen flushing at the temperature         given under a shear of 100 s⁻¹, between two parallel planes 50         mm in diameter.     -   The Mn of the thermoplastic prepolymer or polymer is determined         by potentiometry, size exclusion chromatography or NMR.     -   The measurement of the intrinsic or inherent viscosity is         carried out in m-cresol. The method is well known to those         skilled in the art. Standard ISO 307:2007 is followed, but with         the solvent being changed (use of m-cresol instead of sulfuric         acid), the temperature being changed (20° C.) and the         concentration being changed (0.5% by weight).     -   The glass transition temperature Tg of the thermoplastic         polymers used is measured using a differential scanning         calorimeter (DSC), after a second heating pass, according to         standard ISO 11357-2:2013. The heating and cooling rate is 20°         C./min.     -   The melting temperature Tm and the crystallization temperature         Tc are measured by DSC, after a first heating, according to         standard ISO 11357-3:2013. The heating and cooling rate is 20°         C./min.     -   The enthalpy of crystallization of said matrix polymer is         measured by differential scanning calorimetry (DSC) according to         standard ISO 11357-3:2013.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the differences in the viscosities of a PA₁ and a PA₁-All₁-PA₁ obtained respectively at T₂ and T₃ starting from a PA₁ and a PA₁-All₁-PA₁ of the same average molecular weight Mn₁ having and exhibiting the same viscosity η₁ at the temperature T₁ greater than or equal to T_(m) or T_(g). It is observed that the viscosity of η′₂ of PA₁-All₁-PA₁ is lower than that (η₂) of PA₁ for the same temperature T₂, greater than T₁, and that the viscosity of η′₃ of PA₁-All₁-PA₁ is lower than that (η₃) of PA₁ for the same temperature T₃ greater than T₁ and that the ratio η′₃/η₃<η′₂/η₂.

FIG. 2 shows the change in viscosity with the temperature of example E according to the invention and of comparative example CE 1. It is observed that the viscosity of the polymer according to the invention is lower than that of the comparative polymer for T>T₁.

DETAILED DESCRIPTION Examples A—Preparation of a Polyamide Polymer by Chain Extension of a Reactive Prepolymer (or Oligomer) A-1 Preparation of the Reactive Prepolymer P(X₁)n

This procedure is representative of all the types of polyamide of the invention.

5 kg of the following starting materials are placed in a 14-liter autoclave reactor:

-   -   500 g of water,     -   the diamines,     -   the amino acids or lactams,     -   the diacids,     -   35 g of sodium hypophosphite in solution,     -   0.1 g of a Wacker AK1000 antifoam (the company Wacker         Silicones).

The nature and molar ratios of the molecular units and structures of the reactive prepolymer polyamides (by reference test) are given in table 1 below.

The closed reactor is purged of its residual oxygen and then heated to a temperature of 230° C. of the material. After stirring for 30 minutes under these conditions, the pressurized vapor that has formed in the reactor is gradually reduced in pressure over the course of 60 minutes, while at the same time gradually increasing the temperature of the material such that it becomes established at a minimum of Tm+10° C. at atmospheric pressure for the semicrystalline polymers of Tm>230° C., or 250° C. for the other polymers.

The oligomer (prepolymer) is then emptied out by the bottom valve and then cooled in a water bath and then ground.

The characteristics are presented in table 1 below.

TABLE 1 Characteristics of the prepolymers prepared Molecular Acid Mn structure and Tm Tg Tc ΔH number potentiometry Ref molar composition Monomers used X₁ (° C.) (° C.) (° C.) (J/g) meq/kg(*) g/mol Prepo1 11 Aminoundecanoic acid COOH 178.8 43.2 155 75 809 2472 Adipic acid (1 molecule per chain) Prepo2 11/6T/10T Aminoundecanoic acid COOH 267.8 99 234.5 60 740 2701 (9.1/27.3/63.6) hexamethylenediamine decanediamine terephthalic acid Prepo3 6I/10I hexamethylenediamine COOH (**) 94.5 (**) (**) 900 2222 (30/70) decanediamine isophthalic acid Prepo4 MXDT/10T m-xylylenediamine COOH 270.3 119.4 240.8 50.1 621 3221 (41.2/58.8) decanediamine terephthalic acid (*): Milliequivalents per kilogram (**) Amorphous polymer A-2 Preparation of the Polyamide Polymer (PA₁-All₁-PA₁) by Chain Extension with an Extender of Y₁-A-Y₁ Type

10 g of the dried and ground above prepolymer are mixed with a stoichiometric amount of 1,3-phenylene-bis(2-oxazoline) (PBO). The stoichiometric amount was determined relative to the molar mass determined by NMR.

The mixture is introduced under nitrogen flushing into a DSM co-rotating conical screw microextruder (15 ml volume) preheated to T₁, as defined in the invention, with rotation of the screws at 100 rpm. The mixture is left to recirculate in the microextruder and the increase in viscosity is monitored by measuring the normal force. After approximately 2 minutes, a plateau is reached and the contents of the microextruder are emptied out in the form of a rod. The air-cooled product is formed into granules.

The characteristics are presented in table 2 below.

TABLE 2 Analytical characteristics of the polyamides obtained with chain extension (PA₁-All₁-PA₁) Mn 1 (determined by size exclusion chromatography in Pre- T₁ Tm Tg Tc Δ H PMMA equivalent) Ref polymer (° C.) (° C.) (° C.) (° C.) (J/g) (g/mol) E1 According Prepo1 200 174.7 34 142.8 57 28100 to the invention E2 According Prepo2 280 262.7 114 224 46 12600 to the invention E3 According Prepo3 200 (*) 110 (*) (*) 28500 to the invention E4 According Prepo4 280 273 135 230.5 36 9900 to the invention (*) Amorphous polymer

A-3 Preparation of the Comparative Examples PA₁

The comparative polyamides free of chain extenders PA₁ are synthesized according to a protocol similar to the reactive prepolymers P(X₁)n: this procedure is representative of all the types of polyamide of the invention.

The molar mass of the comparative polymer Mn₁ is adjusted according to an excess of diamine or diacid, according to the method well known to those skilled in the art.

5 kg of the following starting materials are placed in a 14-liter autoclave reactor:

-   -   500 g of water,     -   the diamines,     -   the amino acids or lactams,     -   the diacids,     -   35 g of sodium hypophosphite in solution,     -   0.1 g of a Wacker AK1000 antifoam (the company Wacker         Silicones).

The nature and molar ratios of the molecular units and structures of the comparative polyamides (by reference test) are given in table 3 below.

The closed reactor is purged of its residual oxygen and then heated to a temperature of 230° C. of the material. After stirring for 30 minutes under these conditions, the pressurized vapor that has formed in the reactor is gradually reduced in pressure over the course of 60 minutes, while at the same time gradually increasing the temperature of the material such that it becomes established at a minimum of Tm+10° C. at atmospheric pressure for the semicrystalline polymers of Tm>230° C., or 250° C. for the other polymers.

The polymer is then emptied out by the bottom valve and then cooled in a water bath and then ground.

The characteristics are presented in table 3 below.

TABLE 3 Analytical characteristics of the comparative polyamides free of chain extenders PA₁ Mn 1 (determined by size exclusion Molecular chromatography structure and in PMMA molar Monomers Tm Tg Tc Δ H equivalent) Ref composition used (° C.) (° C.) (° C.) (J/g) (g/mol) CE1 Comparative 11 Aminoundecanoic acid 188.5 47.3 158.4 72.4 28250 (100) Adipic acid (1 molecule per chain) CE2 Comparative 11/6T/10T Aminoundecanoic acid 268.5 114 236 58 12580 (9.1/27.3/63.6) hexamethylenediamine decanediamine terephthalic acid CE3 Comparative 6I/10I hexamethylenediamine (*) 108.3 (*) (*) 28540 (30/70) decanediamine isophthalic acid CE4 Comparative MXDT/10T m-xylylenediamine 279.2 130.7 43.6 241.4 10000 (41.2/58.8) decanediamine terephthalic acid (*) Amorphous polymer

A-4 Comparison of the Viscosities of the PAs According to the Invention and the Comparative PAs

The viscosities of the polymers according to the invention (PA₁-All₁-PA₁) and of the comparative polyamides free of chain extenders PA₁ are reported in tables 4 to 7 below:

TABLE 4 Viscosities of tests E1 and CE1 (PA 11) T Viscosity E1 Viscosity CE1 (° C.) (Pa · s) (Pa · s) 200 756.4 751.2 225 128.2 340.6 250 22.51 166.5 275 5.72 86.9 300 1.75 48 These results are represented in FIG. 2 .

TABLE 5 Viscosities of tests E2 and CE2 (PA 11/6T/10T) T Viscosity E2 Viscosity CE2 (° C.) (Pa · s) (Pa · s) 280 188 186 300 49.4 120

TABLE 6 Viscosities of tests E3 and CE3 (PA 61/101) T Viscosity E3 Viscosity CE3 (° C.) (Pa · s) (Pa · s) 200 42080 42150 250 423 12600

TABLE 7 Viscosities of tests E4 and CE4 (PA MXDT/10T) T Viscosity E4 Viscosity CE4 (° C.) (Pa · s) (Pa · s) 280 187 189 300 46.2 126 The results clearly show that the melt viscosities of the PAs according to the invention are lower than those of the comparative PAs for temperatures T>T₁.

Embodiments

-   1. A composition, comprising at least one polyamide polymer derived     from at least one reactive polyamide prepolymer comprising at least     one chain extender (PA₁-All₁-PA₁), said polyamide polymer being     prepared at a temperature T₁ greater than or equal to the     temperature T_(m) or T_(g) of said polymer, determined respectively     according to standards ISO 11357-3 and ISO 11357-2, and having an     average molecular weight Mn₁, as determined by size exclusion     chromatography,     -   characterized in that said composition has a melt viscosity         which can be modulated according to the temperature to which         said composition is subjected,     -   said temperature being included from T₂ to T₃, T₂ and T₃ being         greater than T₁, and said melt viscosity η′₂ or η′₃ observed         respectively at the temperature T₂ or T₃ being less than the         melt viscosity η₂ or η₃ of said polyamide polymer, free of chain         extender and having the same average molecular weight Mn₁ (PA₁)         observed at the same temperature T₂ or T₃,     -   and with:     -   said composition comprising or consisting of one or more         polyamides, including random or block copolyamides which are         polymers and which comprise different amide units of formula         A/(B)_(r)/(C)_(s), selected as follows:         -   A: is a repeating amide unit chosen from lactams or an amino             acid of C₆-C₁₄, an amide unit X.Y in which X represents at             least one diamine, said diamine being chosen from a linear             or branched aliphatic diamine, a cycloaliphatic diamine and             an aromatic diamine or a mixture thereof, and Y represents             at least one dicarboxylic acid, said diacid being chosen             from:     -   an aliphatic diacid, a cycloaliphatic diacid and an aromatic         diacid,     -   said diamine and said diacid comprising from 4 to 36 carbon         atoms, advantageously from 6 to 18 carbon atoms;         -   B and C: are repeating amide units different than A,             optionally present depending on the value of r and s, r=0 or             1, s=0 or 1, said amides units B and C being chosen from the             same constituents as for A, on the condition that when r and             s=1, then B and C are different,         -   the sum of the units A+B+C being equal to 100% by weight,         -   said composition comprising or consisting of a polyamide             polymer resulting from the polymerization of the reaction             product of:         -   a1) at least one prepolymer of said thermoplastic polyamide             polymer, bearing n reactive end functions X₁, chosen from             NH₂ and —CO₂H with n being 1 to 3, preferably from 1 to 2,             more preferentially 1 or 2, more particularly 2, with         -   a2) at least one chain extender Y₁-A′-Y₁, with A′ being a             hydrocarbon-based biradical of non-polymeric structure,             bearing 2 identical end reactive functions Y₁, reactive by             polyaddition with at least one function X of said prepolymer             a1), preferably having a molecular weight of less than 500,             more preferentially less than 400,         -   in particular, Y₁ is chosen from: oxazine, oxazoline,             oxazolinone, oxazinone, imidazoline, epoxy, maleimide,             cyclic anhydride, and preferentially X₁ is CO₂H and Y₁ is             chosen from an epoxy and an oxazoline,         -   said composition being free of reinforcing fibers and also             of polymeric chain extender. -   2. The composition as in embodiment 1, characterized in that the     ratio of melt viscosity η′₃/η₃ observed at a temperature T₃ is lower     than the ratio of melt viscosity η′₂/η₂ observed at a temperature     T₂, T₃≥T₂+10° C. -   3. The composition as in embodiment 1, characterized in that the     ratio of melt viscosity η′₃/η₃ observed at a temperature T₃ is     higher than the ratio of melt viscosity η′₂/η₂ observed at a     temperature T₂, T₃≤T₂−10° C. -   4. The composition as in one of embodiments 1 to 3, characterized in     that A is an amide unit present in a molar content of 100%, and     represents an aliphatic repeating unit obtained from a lactam or an     amino acid, in particular chosen from PA6, PA11 and PA12. -   5. The composition as in one of embodiments 1 to 3, characterized in     that A is an amide unit present in a molar content of 100%, and     represents a repeating amide unit X.Y, in particular chosen from     PA6.6, PA6.10, PA6.12, PA10.10 and 10.12. -   6. The composition as in one of embodiments 1 to 5, characterized in     that:     -   A is an amide unit present in a molar content ranging from 1% to         99%, B is an amide unit different than A, said unit B being         present in a molar content ranging from 1% to 99%, and C is an         optional amide unit different than A and than B and as defined         above. -   7. The composition as in embodiment 6, characterized in that:     -   A: is a major amide unit present in a molar content ranging from         55% to 95%, preferably from 55% to 85%, more preferentially from         55% to 80%, chosen from x.T units, where x is a linear aliphatic         C₄ to C₁₈ diamine, preferably chosen from C₆, C₉, C₁₀, C₁₁ and         C₁₂ and where T is terephthalic acid,     -   B: is an amide unit different than A, said unit B being present         in a molar content ranging from 5% to 45%, preferably from 15%         to 45%, more preferentially from 20% to 45%, depending on the         T_(m) of the polyamide based on unit A, and said amide unit B is         chosen from an aliphatic repeating unit obtained from a lactam         or an amino acid, in particular chosen from PA6, PA11 and PA 12         or a repeating amide unit X.Y, in particular chosen from PA6.6,         PA6.10, PA6.12, PA10.10 and 10.12. -   8. The composition as in embodiment 6, characterized in that:     -   A: is a major amide unit present in a molar content ranging from         55% to 95%, preferably from 55% to 85%, more preferentially from         55% to 80%, chosen from x.T units, where x is a linear aliphatic         C₄ to C₁₈ diamine, preferably chosen from C₆, C₉, C₁₀, C₁₁ and         C₁₂ and where T is terephthalic acid,     -   B: is an amide unit different than A, said unit B being present         in a molar content ranging from 5% to 45%, preferably from 15%         to 45%, more preferentially from 20% to 45%, depending on the         T_(m) of the polyamide based on unit A and said amide unit B is         chosen from x′.T units where x′ is chosen from:         -   B1) a branched aliphatic diamine bearing a single methyl or             ethyl branch (or branching) and having a main chain length             different by at least two carbon atoms compared with the             main chain length of the diamine x of said associated unit             A, preferably x′ being 2-methylpentamethylenediamine (MPMD)             or         -   B2) m-xylylenediamine (MXD) or         -   B3) a linear aliphatic C₄ to C₁₈ diamine,     -   and preferably, B being chosen from x′.T, where x′ is MPMD         according to B1) or MXD according to B2) or a linear aliphatic         diamine as defined above according to B3) and more         preferentially x′ is MPMD according to B1) or MXD according to         B2) and even more preferentially MXD according to B2),     -   C: optional amide unit different than A and than B, chosen from         amide units based on a cycloaliphatic and/or aromatic structure         or based on x′T as defined above for B but with x′ different         than x′ for the unit B,     -   and under the condition that the sum of the molar contents of         A+B+C is equal to 100%. -   9. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that said amide unit C is present in a molar     content ranging up to 30% relative to the total molar content of the     polyamide polymer, in particular up to 25%, particularly up to 20%,     in particular up to 15%. -   10. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that said amide unit A is present with a molar     content ranging from 55% to 80%, preferably from 55% to 75%, more     preferentially from 55% to 70%, relative to all of the units of said     polymer. -   11. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that said unit B corresponds to x′ T with x′ chosen     according to option B1), in particular with x′ being MPMD. -   12. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that said unit B corresponds to x′ T with x′ chosen     according to option B2), x′ being MXD. -   13. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that said unit B corresponds to a linear aliphatic     diamine according to option B3). -   14. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that the units A and B are selected as follows:     -   for the unit A, which is 6T, said unit B is selected from: 9T,         10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, preferably 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T,         MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a         molar content of B ranging from 20% to 45%,     -   for the unit A, which is 9T, said unit B is selected from: 6T,         10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, preferably 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T,         MPMD.T and MXD.T, more preferentially MPMD.T or MXD.T, with a         molar content of B ranging from 30% to 45%,     -   for the unit A, which is 10T, said unit B is selected from: 6T,         9T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         preferably 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, more preferentially MPMD.T or MXD.T, with a molar content         of B ranging from 25% to 45%,     -   for the unit A, which is 11T, said unit B is selected from: 6T,         9T, 10T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         preferably 9T, 13T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         more preferentially MPMD.T or MXD.T, with a molar content of B         ranging from 20% to 45%,     -   for the unit A, which is 12T, said unit B is selected from: 6T,         9T, 10T, 11T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T,         preferably 9T, 10T, 14T, 15T, 16T, 17T and 18T, MPMD.T and         MXD.T, more preferentially MPMD.T or MXD.T, with a molar content         of B ranging from 20% to 45%. -   15. The composition as in embodiment 14, characterized in that the     unit A is a unit 6T and said unit B is selected from: 9T, 10T, 11T,     12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably     11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more     preferentially MPMD.T or MXD.T, with a molar content of B ranging     from 20% to 45%. -   16. The composition as in embodiment 14, characterized in that the     unit A is a unit 9T and the unit B is selected from: 10T, 11T, 12T,     13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 11T,     12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more     preferentially MPMD.T or MXD.T, with a molar content of B ranging     from 30% to 45%. -   17. The composition as in embodiment 14, characterized in that the     unit A is a unit 10T and the unit B is selected from: 9T, 11T, 12T,     13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 12T,     13T, 14T, 15T, 16T, 17T and 18T, MPMD.T, more preferentially MPMD.T     or MXD.T and MXD.T, with a molar content of B ranging from 25% to     45%. -   18. The composition as in embodiment 14, characterized in that the     unit A is a unit 11T and the unit B is selected from: 9T, 10T, 12T,     13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 9T,     13T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially     MPMD.T or MXD.T, with a molar content of B ranging from 20% to 45%. -   19. The composition as in embodiment 14, characterized in that the     unit A is a unit 12T and the unit B is selected from: 10T, 11T, 13T,     14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, preferably 9T, 10T,     14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, more preferentially     MPMD.T or MXD.T, with a molar content of B ranging from 20% to 45%. -   20. The composition as in one of embodiments 1 to 3 and 6 to 8,     characterized in that:     -   the unit A is x.T, x being a C₄ to C₁₈, preferably C₆, C₉, C₁₀,         C₁₁ or C₁₂, linear aliphatic diamine,     -   the unit B corresponds to x′.T with x′ being B3) a C₄ to C₁₈         linear aliphatic diamine, and     -   the unit C is present and in particular chosen from: C₆ to C₁₂,         preferably C₆, C₁₁ and C₁₂, amino acids or lactams, or mixtures         thereof, or units derived from the reaction of a C₆ to C₁₈,         preferably C₆ to C₁₂, linear aliphatic diacid and of a C₆ to         C₁₈, preferably C₆ to C₁₂, linear aliphatic diamine, and         preferably with the units A and B being respectively based on         the diamines x and x′ as defined in embodiments 1 to 3. -   21. The composition as in embodiment 20, characterized in that said     amide unit C is present in a molar content ranging up to 40%. -   22. The composition as in embodiment 21, characterized in that the     unit C is in a molar content of less than 40%, in particular less     than 30%, in particular less than 20%, relative to the total molar     content of the polyamide. -   23. The composition as in embodiment 21 or 22, characterized in that     the units A, B and C are respectively 10.T/6.T/11. -   24. The composition as in one of embodiments 1 to 23, characterized     in that said reactive prepolymers of said composition a) have a     number-average molecular weight Mn ranging from 500 to 10 000,     preferably from 1000 to 6000. -   25. The composition as in one of embodiments 1 to 24, characterized     in that said polyamide polymer has an average molecular weight which     can be modulated according to the temperature to which said     polyamide polymer is subjected. -   26. The composition as in one of embodiments 1 to 25, characterized     in that said chain extender Y₁-A′-Y₁ is     1,3-phenylene-bis(2-oxazoline) or 1,4-phenylene-bis(2-oxazoline). -   27. A polyamide polymer derived from a polyamide prepolymer     comprising a chain extender, as defined in one of embodiments 1 to     26. -   28. The use of at least one polyamide polymer as defined in     embodiment 27, for modulating the melt viscosity of a composition     comprising said polyamide polymer. -   29. The use as in embodiment 28, for modulating the melt viscosity     of a composition comprising said polyamide polymer and the average     molecular weight of said polyamide polymer. -   30. The use as in embodiment 28 or 29, characterized in that said     chain extender Y₁-A′-Y₁ is chosen from phenylene-bisoxazolines,     preferably 1,3-phenylene-bis(2-oxazoline) or     1,4-phenylene-bis(2-oxazoline). -   31. The use of a composition as defined in one of embodiments 1 to     26, for extrusion, injection-molding, or molding for the manufacture     of mechanical or structural parts based on a composite material, and     in particular for easier impregnation of reinforcing fibers for the     manufacture of composite. -   32. The use as in embodiment 31, characterized in that said     mechanical or structural parts of said composite material concern     applications in the motor vehicle, electrical or electronics,     railway, marine (maritime) and wind power fields, the photovoltaic     field, the solar energy field, including solar panels and components     of solar power stations, the sport field, the aeronautical and     aerospace field, and the road transport (regarding trucks),     construction, civil engineering, panel and leisure fields. -   33. A process for manufacturing a thermoplastic composite material,     in particular a mechanical part or a structural part based on said     material, having a composition as defined in one of embodiments 1 to     26, characterized in that it comprises at least one step of molding     or of processing at least one composition as defined in embodiments     1 to 26, at a temperature T which makes it possible to obtain a     desired viscosity q. -   34. The process as in embodiment 33, characterized in that it     comprises the following steps:     -   i) melt impregnation of a fibrous reinforcement with a         composition as defined in one of embodiments 1 to 26 but not         comprising fibrous reinforcement, in an open or closed mold or         outside the mold, in order to obtain fibers impregnated with         said composition,     -   ii) processing or molding of said composition of step i), so as         to form the final composite part in a mold or with another         processing system. -   35. The process as in embodiment 34, characterized in that said     processing is carried out according to an RTM, S-RIM,     injection-compression molding or pultrusion process or by infusion     molding. -   36. The process as in embodiment 34, characterized in that said     processing is carried out according to a process of     thermocompression of a pre-impregnate under reduced pressure. -   37. A thermoplastic composite material, characterized in that it     results from the use of at least one composition for thermoplastic     composite material as defined in one of embodiments 1 to 26. -   38. A mechanical or structural part made from thermoplastic     composite material, characterized in that it results from the use of     at least one composition as defined in one of embodiments 1 to 26 or     from the use of a polyamide polymer as defined in one of embodiments     28 to 30, or that it is based on a composite material as defined in     embodiment 37 or that it is obtained by means of a process as     defined in either of embodiments 34 and 35. -   39. The structural part as in embodiment 38, characterized in that     it is a motor vehicle part post-treated by cataphoresis. -   40. The part as in embodiment 38, characterized in that it is a part     for wind power. -   41. The part as in embodiment 38, characterized in that it is part     for the aeronautical industry. 

1. A composition, comprising at least one polyamide polymer derived from at least one reactive polyamide prepolymer comprising at least one chain extender (PA₁-All₁-PA₁), said polyamide polymer being prepared at a temperature T₁ greater than or equal to the temperature T_(m) or T_(g) of said polymer, determined respectively according to standards ISO 11357-3 and ISO 11357-2, and having an average molecular weight Mn₁, as determined by size exclusion chromatography, wherein said composition has a melt viscosity which can be modulated according to the temperature to which said composition is subjected, said temperature being included from T₂ to T₃, T₂ and T₃ being greater than T₁, and said melt viscosity η′₂ or η′₃ observed respectively at the temperature T₂ or T₃ being less than the melt viscosity η₂ or η₃ of said polyamide polymer, free of chain extender and having the same average molecular weight Mn₁ (PA₁) observed at the same temperature T₂ or T₃, and with: said composition comprising or consisting of one or more polyamides, including random or block copolyamides which are polymers, and which comprise different amide units of formula A/(B)_(r)/(C)_(s), selected as follows: A is a repeating amide unit chosen from lactams or an amino acid of C₆-C₁₄, an amide unit X.Y in which X represents at least one diamine, said diamine being chosen from a linear or branched aliphatic diamine, a cycloaliphatic diamine and an aromatic diamine or a mixture thereof, and Y represents at least one dicarboxylic acid, said diacid being chosen from: an aliphatic diacid, a cycloaliphatic diacid and an aromatic diacid, said diamine and said diacid comprising from 4 to 36 carbon atoms; B and C are repeating amide units different than A, optionally present depending on the value of r and s, r=0 or 1, s=0 or 1, said amides units B and C being chosen from the same constituents as for A, on the condition that when r and s=1, then B and C are different, the sum of the units A+B+C being equal to 100% by weight, and said composition comprising or consisting of a polyamide polymer resulting from the polymerization of the reaction product of: a1) at least one prepolymer of said thermoplastic polyamide polymer, bearing n reactive end functions X₁, chosen from NH₂ and —CO₂H with n being 1 to 3, with a2) at least one chain extender Y₁-A′-Y₁, with A′ being a hydrocarbon-based biradical of non-polymeric structure, bearing 2 identical end reactive functions Y₁, reactive by polyaddition with at least one function X of said prepolymer a1), Y₁ is chosen from: oxazine, oxazoline, oxazolinone, oxazinone, imidazoline, epoxy, maleimide, and cyclic anhydride, and said composition being free of reinforcing fibers and also of polymeric chain extender, wherein: A is present in a molar content ranging from 55% to 95%, chosen from x.T units, wherein x is a linear aliphatic C₄ to C₁₈ diamine, and wherein T is terephthalic acid, B is present in a molar content ranging from 5% to 45%, depending on the T_(m) of the polyamide based on unit A and B is chosen from x′.T units wherein x′ is chosen from: B1) a branched aliphatic diamine bearing a single methyl or ethyl branch (or branching) and having a main chain length different by at least two carbon atoms compared with the main chain length of the diamine x of said associated unit A, or B2) m-xylylenediamine (MXD) or B3) a linear aliphatic C₄ to C₁₈ diamine, and C is an optional amide unit different than A and B, chosen from amide units based on a cycloaliphatic and/or aromatic structure or based on x′T as defined for B but with x′ different than x′ for the unit B, and under the condition that the sum of the molar contents of A+B+C is equal to 100%.
 2. The composition of claim 1, wherein B corresponds to x′ T with x′ chosen according to option B1).
 3. The composition of claim 1, wherein B corresponds to x′ T with x′ chosen according to option B2), x′ being MXD.
 4. The composition of claim 1, wherein B corresponds to a linear aliphatic diamine according to option B3).
 5. The composition of claim 1, wherein: A is x.T, x being a C₄ to C₁₈ linear aliphatic diamine, B corresponds to x′.T with x′ being B3) a C₄ to C₁₈ linear aliphatic diamine, and C is present and chosen from: C₆ to C₁₂ amino acids or lactams, or mixtures thereof, or units derived from the reaction of a C₆ to C₁₈ linear aliphatic diacid and of a C₆ to C₁₈ linear aliphatic diamine, and preferably with the units A and B being respectively based on the diamines x and x′.
 6. The composition of claim 5, wherein C is present in a molar content ranging up to 40%.
 7. The composition of claim 6, wherein C is in a molar content of less than 40%, relative to the total molar content of the polyamide.
 8. The composition of claim 6, wherein A, B and C are respectively 10.T/6.T/11.
 9. The composition of claim 1, wherein the ratio of melt viscosity η′₃/η₃ observed at a temperature T₃ is lower than the ratio of melt viscosity η′₂/η₂ observed at a temperature T₂, T₃≥T₂+10° C.
 10. The composition of claim 1, wherein the ratio of melt viscosity η′₃/η₃ observed at a temperature T₃ is higher than the ratio of melt viscosity η′₂/η₂ observed at a temperature T₂, T₃≤T₂−10° C.
 11. The composition of claim 1, wherein C is present in a molar content ranging up to 30% relative to the total molar content of the polyamide polymer.
 12. The composition of claim 1, wherein A is present with a molar content ranging from 55% to 80%, relative to all of the units of said polymer.
 13. The composition of claim 1, wherein A and B are selected as follows: when A is 6T, B is selected from: 9T, 10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 20% to 45%, when A is 9T, B is selected from: 6T, 10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 30% to 45%, when A is 10T, B is selected from: 6T, 9T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 25% to 45%, when A is 11T, B is selected from: 6T, 9T, 10T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 20% to 45%, and when A is 12T, B is selected from: 6T, 9T, 10T, 11T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 20% to 45%.
 14. The composition of claim 13, wherein A is 6T and B is selected from: 9T, 10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 20% to 45%.
 15. The composition of claim 13, wherein A is 9T and B is selected from: 10T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 30% to 45%.
 16. The composition of claim 13, wherein A is 10T and B is selected from: 9T, 11T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 25% to 45%.
 17. The composition of claim 13, wherein A is 11T and B is selected from: 9T, 10T, 12T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 20% to 45%.
 18. The composition of claim 13, wherein A is 12T and B is selected from: 10T, 11T, 13T, 14T, 15T, 16T, 17T and 18T, MPMD.T and MXD.T, with a molar content of B ranging from 20% to 45%.
 19. The composition of claim 1, wherein said reactive polyamide prepolymer has a number-average molecular weight Mn ranging from 500 to 10,000.
 20. The composition of claim 1, wherein said reactive polyamide polymer has an average molecular weight which can be modulated according to the temperature to which said polyamide polymer is subjected.
 21. The composition of claim 1, wherein said chain extender Y₁-A′-Y₁ is 1,3-phenylene-bis(2-oxazoline) or 1,4-phenylene-bis(2-oxazoline). 